GENERAL:
THE MOST WIDELY USED CHROMIUM NICKEL AUSTENITIC STAINLESS STEEL . IT IS
NON MAGNETIC IN ANNEALED CONDITION . WHEN COLD WORKED IT BECOMES SLIGHTLY MAGNETIC.
USES:
SUITABLE FOR FABRICATING AND WELDING.
CHEMICAL
ANALYSIS: |
C |
SI |
MN |
S |
P |
0.030MAX |
1.00MAX |
2.00MAX |
0.030MAX |
0.045MAX |
|
Cr |
Ni |
|
|
|
17.00/19.00 |
9.0/12.0 |
|
|
|
|
TYPICAL
MECHANICAL PROPERTIES: (EXAMPLE ONLY) |
TEN. STRENTH |
YIELD STRESS |
ELONG |
480Nmm |
2 215Nmm |
2 40%min |
HEAT TREATMENT & CONDITION
NON HARDENABLE BY HEAT TREATMENT.
SECTIONS
COMMERCIALY AVAILABLE IN ROUNDS, HEXAGONS, AND FLATS.
RELATED SPECIFICATIONS
AISI 304 304L BS 970 316S31